Damage production in carbide single crystals irradiated with MeV heavy ions

S. Pellegrino 1 L. Thomé 2 A. Debelle 2 S. Miro 3 P. Trocellier 3
1 INSTN - Institut National des Sciences et Techniques Nucléaires
2 CSNSM PCI
CSNSM - Centre de Spectrométrie Nucléaire et de Spectrométrie de Masse
3 SRMP - Service de recherches de métallurgie physique
Abstract : Carbide (SiC, TiC, and ZrC) single crystals were irradiated at room temperature with MeV Au ions. The damage created by irradiation was evaluated by RBS-C, XRD, and Raman experiments. The results indicate a different radiation behavior of TiC and ZrC as compared with SiC. The accumulation of defects created by nuclear collisions leads to amorphization of SiC at the lowest Au fluence used (2.8 × 1014 cm−2), whereas TiC and ZrC do not amorphize at the highest Au fluence used (3.3 × 1015 cm−2). The different properties of TiC and ZrC carbides versus SiC could be related to differences in the nature of the chemical bonds in TiC and ZrC versus SiC.
keyword : TiC ZrC SiC Carbides RBS-C XRD Raman spectroscopy
Document type :
Journal articles
Complete list of metadata
http://hal.in2p3.fr/in2p3-00799087
Contributor : Christine Hadrossek Connect in order to contact the contributor
Submitted on : Monday, March 11, 2013 - 3:14:15 PM
Last modification on : Tuesday, December 14, 2021 - 3:48:00 AM

Identifiers

Collections

IN2P3 | CEA | CSNSM | CNRS | DEN | DEN-SACLAY

Citation

S. Pellegrino, L. Thomé, A. Debelle, S. Miro, P. Trocellier. Damage production in carbide single crystals irradiated with MeV heavy ions. Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms, Elsevier, 2013, article in press, ⟨10.1016/j.nimb.2012.11.091⟩. ⟨in2p3-00799087⟩

Export

BibTeX TEI DC DCterms EndNote

Share

Metrics

Les métriques sont temporairement indisponibles