Journal of Nuclear Materials 425 (2012) 193-196

Structure and mechanical properties of swift heavy ion irradiated tungsten-bearing delta-phase oxides Y6W1O12 and Yb6W1O12

M. Tang, T. A. Wynn, M. K. Patel, J. Won, I. Monnet1, J. C. Pivin2, N. A. Mara, K. E. Sickafus

(2012)

We report on the relationship between structure and mechanical properties of complex oxides whose structures are derivatives of fluorite, following irradiation with swift heavy ion (92 MeV Xe) which approximately simulates fission product irradiation, where the electronic energy loss dominates. The two compounds of interest in this paper are Y6W1O12 and Yb6W1O12. These compounds possess an ordered, fluorite derivative crystal structure known as the delta (delta) phase, a rhombohedral structure belonging to space group R (3) over bar.

1 :	CIMAP - Centre de recherche sur les Ions, les MAtériaux et la Photonique
2 :	CSNSM - Centre de Spectrométrie Nucléaire et de Spectrométrie de Masse

équipe(s) de recherche : CSNSM PCI

Thème(s)

:

Physique/Matière Condensée/Science des matériaux

Mot(s)-clé(s) : INDUCED AMORPHIZATION – NUCLEAR-WASTE – RADIATION – IMMOBILIZATION – TRANSFORMATION – PLUTONIUM – CERAMICS

in2p3-00716297, version 1

http://hal.in2p3.fr/in2p3-00716297

oai:hal.in2p3.fr:in2p3-00716297

Contributeur : Christine Hadrossek <>

Soumis le : Mardi 10 Juillet 2012, 12:08:25

Dernière modification le : Mercredi 11 Juillet 2012, 11:24:33