Structural effect of heavy ion irradiation on GdBaCuO ceramics
Ruault M.-O., Bernas H., Gasgnier M., Levet J.-C., Noel H. et al
Revue de Physique Appliquee 25, 1 (1990) 49-53 - http://hal.archives-ouvertes.fr/jpa-00246161
Physique/Articles anciens
Structural effect of heavy ion irradiation on GdBaCuO ceramics
M.-O. Ruault1, H. Bernas1, M. Gasgnier, J.-C. Levet, H. Noel, P. Gougeon, M. Potel
1 :  CSNSM - Centre de Spectrométrie Nucléaire et de Spectrométrie de Masse
CNRS : UMR8609 – IN2P3 – Université Paris XI - Paris Sud
batiments 104 et 108 - 91405 Orsay Campus
The influence of twin boundaries as sinks on defects induced by 480 keV Kr ion irradiation in GdBaCuO crystals was observed in situ at 40 and 300 K. The interaction of the dislocations with the twin boundaries followed on a video recording. A crystalline to amorphous transition was observed above a total fluence of ∼ 4 - 5 x 10^12 Kr/cm2. A comparison between orthorhombic (Os) crystals and a monoclinic structure (Ms) (close to Os and whose parameters were calculated) shows that the behaviour of irradiation-induced extended defects does not depend on a small initial deformation of the orthorhombic cell. In both case, an occasional orthorhombic (or monoclinic) to tetragonal phase transition only occurs when the amorphization process has begun.

Revue de Physique Appliquee
non spécifiée
Articles dans des revues avec comité de lecture

amorphisation – barium compounds – dislocations – gadolinium compounds – high temperature superconductors – ion beam effects – solid state phase transformations – twin boundaries – Kr ions – heavy ion irradiation – crystalline to amorphous transition – orthorhombic – monoclinic – tetragonal – phase transition – amorphization – 480 keV – 40 to 300 K – GdBaCuO