Chemistry of Materials 23 (2011) 3072-3085
Unexpected Mechanism of Zn2+ Insertion in Calcium Phosphate Bioceramics
S. Gomes1, J.-M. Nedelec1, E. Jallot2, D. Sheptyakov3, G. Renaudin1
(2011)

Rietveld analysis on X-ray powder diffraction patterns recorded from Zn-doped, Zn/Sr, and Zn/Mg codoped biphasic calcium phosphate (BCP) samples has been used to locate Zn2+ cations in both hydroxyapatite (HAp) and β-tricalcium phosphate (β-TCP) phases heat-treated at 1100 °C. Zn atoms occupy interstitial sites in HAp (Wyckoff site 2b), leading to an insertion solid solution of general composition Ca10Znx(PO4)6O2x(OH)2-2x. Replacement of hydroxyl by O2- anions with formation of linear O-Zn-O entities should be considered to preserve the electroneutrality of the material. Contrary to HAp case, Zn atoms substitute calcium atoms in β-TCP leading to a substitution solid solution of general composition Ca3-xZnx(PO4)2. Micro-Raman spectroscopy and neutron diffraction have confirmed these insertion/substitution mechanisms. The different mechanisms of zinc incorporation should be considered to stabilize the desired calcium phosphate phase which are managed by the Ca/P and (Ca+Zn)/P ratios. Furthermore, discussion of biological properties of Zn-doped calcium phosphate ceramics should take into account the true insertion mechanism as critically discussed here.
1 :  LMI - Laboratoire des Matériaux Inorganiques
2 :  LPC-CLERMONT - Laboratoire de Physique Corpusculaire de Clermont-Ferrand
3 :  Laboratory for Neutron Scattering ETHZ & Paul Scherrer Institut
Sciences du Vivant/Ingénierie biomédicale/Biomatériaux

Physique/Physique/Biophysique

Chimie/Matériaux
biomaterials – zinc doping – calcium phosphates – Rietveld refinement – Raman